RP 450mm Graphite Electrode
The main raw material of graphite electrode production is petroleum coke. A small amount of asphalt coke can be added to ordinary power graphite electrode.
The main raw material of this kind of RP 450mm Graphite Electrode is petroleum coke. A small amount of asphalt coke can be added to ordinary power graphite electrode. The sulfur content of petroleum coke and asphalt coke should not exceed 0.5%. Needle coke is also needed to produce high power or ultra high power graphite electrodes. In addition, it has the prominent features of compact structure, good electrical and thermal conductivity, strong oxidation resistance, corrosion resistance, low resistivity, high current load resistance, low price and high cost effective. It is widely used in the smelting of various metals.
Steel is a big consumer in carbon industry, and graphite electrode has become the golden key for carbon industry to enter the steel field.
| Comparison Technical Specification for RP Graphite Electrode 18" | ||
| Electrode | ||
| Item | Unit | Supplier Spec |
| Typical Characteristics of Pole | ||
| Nominal Diameter | mm | 450 |
| Max Diameter | mm | 460 |
| Min Diameter | mm | 454 |
| Nominal Length | mm | 1800-2400 |
| Max Length | mm | 1900-2500 |
| Min Length | mm | 1700-2300 |
| Bulk Density | g/cm3 | 1.60-1.65 |
| transverse strength | MPa | ≥8.5 |
| Young' Modulus | GPa | ≤9.3 |
| Specific Resistance | µΩm | 7.5-8.5 |
| Maximum current density | KA/cm2 | 13-17 |
| Current Carrying Capacity | A | 22000-27000 |
| (C.T.E) | 10-6℃ | ≤2.4 |
| ash content | % | ≤0.3 |
| Typical Characteristics of Nipple (4TPI/3TPI) | ||
| Bulk Density | g/cm3 | ≥1.74 |
| transverse strength | MPa | ≥16.0 |
| Young' Modulus | GPa | ≤13.0 |
| Specific Resistance | µΩm | 5.8-6.5 |
| (C.T.E) | 10-6℃ | ≤2.0 |
| ash content | % | ≤0.3 |